Outperforms the Competition
KetaSpire® PEEK (polyetheretherketone) offers the best combination of fatigue resistance and chemical resistance, which is similar to PPS (polyphenylene sulfide). However, PEEK can operate at higher temperatures and retains its excellent mechanical properties at continuous-use temperatures up to 240 °C (464 °F), allowing it to replace metal in severe end-use environments. Glass fiber-reinforced and carbon fiber-reinforced grades provide a wide range of performance options.
KetaSpire® AM FILAMENT CF10 LS1 POLYETHERETHERKETONE (PEEK) 1KG
Ketaspire® PEEK AM Filament CF10 LS1 incorporates 10% carbon fiber reinforcement for increased strength. This material provides long-term performance up to 240°C, including exceptional chemical resistance. These properties make it particularly suited for metal replacement in critical applications in severe end-use environments, such as Oil & Gas, Aerospace and Automotive. Specifications
- Filament Diameter: 1.75mm
- Net Filament Weight: 0.5 or 1kg
- Filament Color: Black
- Storage: place in zip sealed bag with desiccant after use
- Desiccant: Yes
- Processing Temperature Range: 390-420°C
- Recommended Bed Temperature: >200°C
- Drying Conditions: 150°C for at least 4 hours
- Density: 1.33 g/cm3
- Tensile Strength at Break: 140 MPa*
- Tensile Elongation at Break: 1.7%*
- Notched Izod Impact: 89 J/m*
- Melt Temperature: 343°C*
KetaSpire® AM FILAMENT MS NT1 POLYETHERETHERKETONE (PEEK) 500G ON A 0.36KG SP
Ketaspire® PEEK AM Filament MS NT1 provides long-term performance up to 240°C, including exceptional chemical resistance and outstanding wear. These properties make it particularly suited for metal replacement in critical applications in severe end-use environments, such as Oil & Gas, Aerospace and Automotive.
Specifications
- Filament Diameter: 1.75mm
- Net Filament Weight: 0.5 or 1kg
- Filament Color: Beige
- Storage: place in zip sealed bag with desiccant after use
- Desiccant: Yes
- Processing Temperature Range: 390-420°C
- Recommended Bed Temperature: >200°C
- Drying Conditions: 150°C for at least 4 hours
- Density: 1.29 g/cm3*
- Tensile Strength at Yield: 85 MPa*
- Tensile Elongation at Break: 26%*
- Notched Izod Impact: 81 J/m*
- Melt Temperature: 343°C*
Not All PEEK is Created Equal
Not all commercial PEEK products deliver the same level of performance. KetaSpire® PEEK offers distinct performance advantages due to Solvay’s newer polymer production technology. Depending on the grade, KetaSpire® PEEK offers
- Better fatigue resistance
- 20% higher impact strength
- 60% higher ductility
KetaSpire® Product Line
Solvay’s KetaSpire® PEEK product line includes:
- Neat grades (lubricated and non-lubricated)
- Glass fiber and carbon fiber reinforced grades (low and high melt flow)
- Wear resistant SL grades (lubricated and non-lubricated)
- Natural-colored powders (coarse, fine, super-fine and ultra-fine)
Comparison of neat and modified grades
Glass fiber and carbon fiber reinforced KetaSpire® PEEK grades deliver the greater mechanical robustness required for demanding structural applications.
Torsional DMA of neat and fiber reinforced KetaSpire® PEEK
Wear Resistance
Wear properties are enhanced by adding carbon fiber and polymeric lubricants such as PTFE. Torlon® PAI offers the best high-temperature wear resistance.
Torsional DMA of wear-resistant Spire® Ultra Polymers
Comparison of friction and wear grades