SABIC ULTEM™ AM9085F

SABIC
SKU: 68555073861169
$300.00
ULTEM™ AM9085F filament is a high performance polyetherimide blend product manufactured from ULTEM™ 9085 resin. It is available in black and natural (unpigmented) colors. It provides high heat resistance and mechanical strength, is UL94 V-0 compliant at 1.5 and 3.0 mm (Blue Cards are available on UL IQ Database), and meets FAR 25.853 and OSU 55/55 with low toxicity, smoke, and flame evolution.
QTY:

 

Revision: 17/07/2019
PROPERTIES TYPICAL VALUES UNITS TEST METHODS
MECHANICAL
Tensile Modulus
XY ORIENTATION 2176 MPa ASTM D638
XZ ORIENTATION 2555 MPa ASTM D638
ZX ORIENTATION 2439 MPa ASTM D638
Tensile Stress, brk, Type I, 5 mm/min
XY ORIENTATION 62 MPa ASTM D638
XZ ORIENTATION 80 MPa ASTM D638
ZX ORIENTATION 45 MPa ASTM D638
Tensile Strain, brk, Type I, 5 mm/min
XY ORIENTATION 5.1 % ASTM D638
XZ ORIENTATION 5.8 % ASTM D638
ZX ORIENTATION 2.3 % ASTM D638
Flexural Modulus, 1.3 mm/min
XY ORIENTATION 2126 MPa ASTM D 790
XZ ORIENTATION 2550 MPa ASTM D 790
ZX ORIENTATION 2070 MPa ASTM D 790
Izod Impact, notched, 23°C 2)
XY ORIENTATION 104 J/m ASTM D 256
XZ ORIENTATION 100 J/m ASTM D 256
ZX ORIENTATION 33 J/m ASTM D 256
Izod Impact, un-notched, 23°C
XY ORIENTATION 763 J/m ASTM D 256
XZ ORIENTATION 1003 J/m ASTM D 256
ZX ORIENTATION 131 J/m ASTM D 256
THERMAL
HDT, 1.82 MPa, 3.2 mm, unannealed
XY ORIENTATION 175 °C ASTM D648
XZ ORIENTATION 175 °C ASTM D648
ZX ORIENTATION 165 °C ASTM D648
Coefficient of Thermal Expansion - flow
XY ORIENTATION 57.1 µm/(m-°C) ASTM E 831
XZ ORIENTATION 60.6 µm/(m-°C) ASTM E 831
ZX ORIENTATION 62.1 µm/(m-°C) ASTM E 831
Coefficient of Thermal Expansion - x-flow
XY ORIENTATION 58.3 µm/(m-°C) ASTM E 831
XZ ORIENTATION 61.1 µm/(m-°C) ASTM E 831
ZX ORIENTATION 62.9 µm/(m-°C) ASTM E 831
PHYSICAL
Density 1.275 g/cm³ ASTM D 792
ELECTRICAL
Volume Resistivity
XY ORIENTATION 1.07E+15 Ohm-cm ASTM D 257
XZ ORIENTATION 1.1E+15 Ohm-cm ASTM D 257
Dielectric Constant - 100 MHz
XY ORIENTATION 2.54 - ASTM D 150
XZ ORIENTATION 2.73 - ASTM D 150
Dissipation Factor - 100 MHz
XY ORIENTATION 0.00233 - ASTM D 150
XZ ORIENTATION 0.003 - ASTM D 150
Dielectric Constant - 500 MHz
XY ORIENTATION 2.53 - ASTM D 150
XZ ORIENTATION 2.72 - ASTM D 150
Dissipation Factor - 500 MHz
XY ORIENTATION 0.005 - ASTM D 150
XZ ORIENTATION 0.00567 - ASTM D 150
Dielectric Constant - 1000 MHz
XY ORIENTATION 2.52 - ASTM D 150
XZ ORIENTATION 2.71 - ASTM D 150
Dissipation Factor - 1000 MHz
XY ORIENTATION 0.004 - ASTM D 150
XZ ORIENTATION 0.004 - ASTM D 150
FLAME CHARACTERISTICS
FAA Flammability
XY ORIENTATION, 1.5mm PASS - FAR 25.853
OSU total heat release (2 minute test)
XY ORIENTATION, 1.5mm 44 kW-min/m² FAR 25.853
OSU peak heat release rate (5 minute test)
XY ORIENTATION, 1.5mm 45 kW/m² FAR 25.853
UL94 Flame Class Rating 1)
XY ORIENTATION, 1.5mm V-0 - -
XZ ORIENTATION, 1.5mm V-0 - -
ZX ORIENTATION, 1.5mm V-0 - -
XY ORIENTATION, 3.0mm V-0 - -
XZ ORIENTATION, 3.0mm V-0 - -
ZX ORIENTATION, 3.0mm V-0 - -
1) UL results provided herein may not be sufficient to waive end use part testing for UL listing. Contact UL for further details. 2) Izod impact strength test coupons were printed using a Stratasys FORTUS† 900mc printer at high print density (88.5%).